I-JQ.MH00Cr24Ni13 intsimbi yokuwelda intsimbi engaphantsi kwamanzi
Iimbonakalo
Xa kuthelekiswa ne-welding manual, isantya sokubeka sinokunyuswa ngamaxesha angama-2-4, kwaye ukusebenza kakuhle kwe-deposit kuphezulu njenge-90%.
Ukulungelelaniswa kwangoku kunye ne-voltage inkulu, ukusetwa kweemeko ze-welding kulula, kwaye kulula ukwenza i-semi-automatic kunye ne-automatic welding.
Ukususwa kakuhle kwe-slag kunye nomphezulu we-weld weld ekhazimlayo.Ukongeza, kukho i-splash encinci, ukuzinza kwe-arc kuhle kakhulu, kwaye i-X-ray ifanelekile.
Ukwakheka kweekhemikhali zocingo lweWelding(Wt%)
Umzekelo | Ukwakhiwa kweekhemikhali zocingo lokuwelda (Wt%) | ||||||||
C | Mn | Si | Cr | Ni | P | S | Cu | enye | |
JQ.MH00Cr24Ni13 | 0.026 | 1.74 | 0.58 | 23.49 | 12.9 | 0.024 | 0.008 | - | - |
Ukusebenza kwemveliso
Imodeli esemgangathweni ethobelayo (elinganayo). | Umzekelo weempawu ezibonakalayo zentsimbi egciniweyo (kunye ne-SJ601) | ||
GB | AWS | I-Tensile StrengthMPa | Elongation% |
F309L-H00Cr24Ni13 | I-ER309L | 558 | 40.0 |
imveliso welding reference yangoku (AC okanye DC+)
Ububanzi (mm) | ¢2.5 | ¢3.2 | ¢4.0 | ¢5.0 |
Welding current(A) | 400-500 | 450-550 | 500-600 | 550-650 |
IiNkcazo zeMveliso
Idayamitha yocingo | ¢2.5 | ¢3.2 | ¢4.0 | ¢5.0 |
Ubunzima bephakheji | 25/50/100/200/250/300/350Kg/iqhekeza |
Imiqathango yokusetyenziswa kwemveliso
1.Iqondo lobushushu phakathi kweewelds liyacetyiswa ukuba lilawulwe malunga ne-150°C.Xa i-multi-pass multi-layer welding of small and medium-sized sizes, nikela ingqalelo ekulawuleni amandla omgca we-welding.
2.Uluhlu lwe-rust, ukufuma, ioli, uthuli, njl njl. inxalenye ye-welding kufuneka icocwe.
3.I-flux kufuneka ibhakwe kwi-300-350 ℃ i-2h phambi kokusetyenziswa.
Ezi ngcebiso zingentla zezesalathiso kuphela, kwaye eyona meko iya kulawula kumsebenzi othile.Ukuba kuyimfuneko, ukufaneleka kwenkqubo kufuneka kuqhutywe ngaphambi kokumisela isicwangciso se-welding.